Elastollan? 880A-13N
熱塑性聚氨酯彈性體（聚酯）
產(chǎn)品說明:
Elastollan? 880AN is specifically formulated for transparent film applications. It exhibits excellent abrasion resistance, toughness, transparency, and oil/fuel resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan?880AN is supplied uncolored in pellet form.
密度 / 比重 | 1.20 |
| ASTM D792 |
熔流率（熔體流動速率） |
|
| ASTM D1238 |
190°C/3.8 kg | 15 到 25 | g/10 min |
|
190°C/8.7 kg | 40 到 60 | g/10 min |
|
肖氏硬度 (邵氏 A) | 78 |
| ASTM D2240 |
拉伸模量 (注塑) | 3600 | psi | ASTM D412 |
彎曲模量 (注塑) | 3200 | psi | ASTM D790 |
泰伯耐磨性 | 40.0 | mg | ASTM D1044 |
Abrasion - DIN | 10 | mm3 | DIN 53516 |
拉伸應(yīng)力 |
|
| ASTM D412 |
100%應(yīng)變 | 770 | psi |
|
300%應(yīng)變 | 1840 | psi |
|
抗張強度 | 4800 | psi | ASTM D412 |
伸長率 (斷裂) | 610 | % | ASTM D412 |
撕裂強度 2 | 490 | lbf/in | ASTM D624 |
壓縮永久變形 |
|
| ASTM D395B |
73°F, 22 hr | 20 | % |
|
158°F, 22 hr | 50 | % |
|
玻璃轉(zhuǎn)化溫度 | -16.6 | °F | 內(nèi)部方法 |
維卡軟化溫度 | 147 | °F | ASTM D1525 |
Softening Point - DMA | 151 | °F | 內(nèi)部方法 |
干燥溫度 | 212 到 230 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
建議的最大水分含量 | 0.030 | % |
|
料筒后部溫度 | 338 到 410 | °F |
|
料筒中部溫度 | 338 到 410 | °F |
|
料筒前部溫度 | 338 到 410 | °F |
|
射嘴溫度 | 392 到 410 | °F |
|
干燥溫度 | 212 到 230 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
料筒1區(qū)溫度 | 320 到 392 | °F |
|
料筒3區(qū)溫度 | 320 到 392 | °F |
|
料筒5區(qū)溫度 | 320 到 392 | °F |
|
接頭溫度 | 347 到 392 | °F |
|
口模溫度 | 347 到 401 | °F |
|