Radilon? S 40EPT2808 333 NER
聚酰胺6
PA6 high viscosity extrusion grade. Low modulus, high flexibility and high impact strength, even at low temperatures. Black colour.
This material has been designed for extrusion of pipes. Typical application: convoluted fuel pipes for the automotive industry.
特性 | - High Flexibility、抗撞擊性高、耐低溫沖擊、粘度高
|
用途 | - 管道系統(tǒng)、汽車領(lǐng)域的應(yīng)用
|
RoHS 合規(guī)性 | |
外觀 | |
加工方法 | |
樹脂ID (ISO 1043) | |
拉伸模量 | 131000 | -- | psi | ISO 527-2/1A/1 |
拉伸應(yīng)力 (屈服) | 5080 | -- | psi | ISO 527-2/1A/50 |
標(biāo)稱拉伸斷裂應(yīng)變 | > 100 | -- | % | ISO 527-2/1A/50 |
彎曲模量 2 | 79800 | -- | psi | ISO 178 |
彎曲應(yīng)力 2 | 3630 | -- | psi | ISO 178 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 (73°F) | 31 | -- | ft·lb/in2 | ISO 179/1eA |
熱變形溫度 (264 psi, 未退火) | 122 | -- | °F | ISO 75-2/Af |
維卡軟化溫度 | 248 | -- | °F | ISO 306/B50 |
熔融溫度 3 | 428 | -- | °F | ISO 11357-3 |
表面電阻率 4 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
體積電阻率 4 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏電起痕指數(shù) (解決方案 A) | 600 | -- | V | IEC 60112 |
UL 阻燃等級(jí) (0.031 in) | HB | -- |
| UL 94 |
可燃性 | < 1 | -- | in/min | FMVSS 302 |
干燥溫度 - 熱風(fēng)干燥機(jī) | 176 | °F |
|
干燥時(shí)間 - 熱風(fēng)干燥機(jī) | 2.0 到 4.0 | hr |
|
Dew Point - 熱風(fēng)干燥機(jī) | -4 | °F |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 482 到 536 | °F |
|
模具溫度 | 158 到 176 | °F |
|
注射速度 | 中等 |
|
|
熔體溫度 | 464 到 518 | °F |
|
如需蘭蒂奇原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！