Stanyl? TW200FM33
聚酰胺 46
產(chǎn)品說明:
30% Glass/Mineral Reinforced, Heat Stabilized, Low Warpage
Special Features:
Used In:
Stanyl? is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
填料/增強材料 | |
添加劑 | |
特性 | |
加工方法 | |
多點數(shù)據(jù) | |
樹脂ID (ISO 1043) | |
密度 | 1.42 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 1.2 | -- | % |
|
流量 | 0.30 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F | 9.5 | -- | % |
|
平衡, 73°F, 50% RH | 2.6 | -- | % |
|
粘數(shù) | 145 | -- | cm3/g | ISO 307 |
拉伸模量 | 1.13E+6 | 464000 | psi | ISO 527-2 |
拉伸應力 (斷裂) | 20300 | 10200 | psi | ISO 527-2 |
拉伸應變 (斷裂) | 3.0 | 6.0 | % | ISO 527-2 |
簡支梁缺口沖擊強度 |
|
|
| ISO 179/1eA |
-22°F | 1.9 | -- | ft·lb/in2 |
|
73°F | 1.9 | -- | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 554 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 527 | -- | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 2 | 167 | -- | °F | ISO 11357-2 |
維卡軟化溫度 | 554 | -- | °F | ISO 306/B50 |
熔融溫度 2 | 563 | -- | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
| ISO 11359-2 |
流動 | 2.2E-5 | -- | in/in/°F |
|
橫向 | 3.9E-5 | -- | in/in/°F |
|
體積電阻率 | 1.0E+14 | 1.0E+9 | ohms·cm | IEC 60093 |
漏電起痕指數(shù) | 300 | -- | V | IEC 60112 |
可燃性等級 (0.06 in) | HB | -- |
| IEC 60695-11-10, -20 |
干燥溫度 | 176 | °F |
干燥時間 | 4.0 到 8.0 | hr |
料筒后部溫度 | 536 到 608 | °F |
料筒中部溫度 | 572 到 608 | °F |
料筒前部溫度 | 572 到 608 | °F |
射嘴溫度 | 572 到 608 | °F |
加工（熔體）溫度 | 581 到 608 | °F |
模具溫度 | 176 到 248 | °F |
注射速度 | 中等偏快 |
|
背壓 | 290 到 1450 | psi |
螺桿壓縮比 | 2.5:1.0 |
|
如需恩驊力（Envalior）原廠物性表及相關文件，請聯(lián)系我司工作人員，謝謝！