Plexiglas? Satinice df33 zk6BR
聚甲基丙烯酸甲酯-丙烯酸
PLEXIGLAS? Satinice df33 zk6BR, based on PLEXIGLAS? Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.
Typical properties of impact modified PLEXIGLAS? molding compound are
Extruded parts from PLEXIGLAS? Satinice df33 zk6BR are characterized by the following special properties:
Application:
Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry, but also for injection molding items for lighting engineering applications.
Examples:
applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired.
添加劑 | |
特性 | - High Light Diffusion、High Light Transmission、沖擊改性、光澤中、抗撞擊性高、耐氣候影響性能良好、硬度高
|
用途 | - 家具、建筑應用領域、片材、汽車領域的應用、型材、照明漫射器
|
外觀 | |
形式 | |
加工方法 | |
密度 | 1.16 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (230°C/3.8 kg) | 0.0854 | in3/10min | ISO 1133 |
拉伸模量 | 290000 | psi | ISO 527-2/1 |
拉伸應力 (屈服) | 6530 | psi | ISO 527-2/50 |
拉伸應變 (屈服) | 4.0 | % | ISO 527-2/50 |
標稱拉伸斷裂應變 | 25 | % | ISO 527-2 |
簡支梁無缺口沖擊強度 (73°F) | 19 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 210 | °F | ISO 75-2/B |
264 psi, 未退火 | 205 | °F | ISO 75-2/A |
維卡軟化溫度 | 210 | °F | ISO 306/B50 |
線形熱膨脹系數 - 流動 (32 到 122°F) | 5.1E-5 | in/in/°F | ISO 11359-2 |
熱燈絲點火溫度 | 1290 | °F | IEC 60695-2-13 |
Half-Value Angle | 36.0 | ° | DIN 5036 |
Scattering Power | 0.490 |
| DIN 5036 |
干燥溫度 | < 185 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
熔體溫度 | 446 到 500 | °F |
|
口模溫度 | 446 到 500 | °F |
|
如需德固賽原廠物性表及相關文件，請聯系我們工作人員，謝謝！