LEXAN? Copolymer 4701R
聚酯碳酸酯
產(chǎn)品說明:
High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi.
特性 | |
用途 | |
加工方法 | |
多點數(shù)據(jù) | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530)
|
Also Available In | |
密度 / 比重 | |
| ASTM D792 |
特定體積 | 23.0 | in3/lb | ASTM D792 |
熔流率（熔體流動速率） |
|
| ASTM D1238 |
300°C/1.2 kg | 2.0 | g/10 min |
|
300°C/6.1 kg | 9.0 | g/10 min |
|
收縮率 - 流動 (0.126 in) | 8.0E-3 到 0.010 | in/in | 內部方法 |
吸水率 (24 hr) | 0.19 | % | ASTM D570 |
洛氏硬度 |
|
| ASTM D785 |
M 級 | 92 |
|
|
R 級 | 127 |
|
|
抗張強度 2 |
|
| ASTM D638 |
屈服 | 9430 | psi |
|
斷裂 | 11200 | psi |
|
伸長率 2 (斷裂) | 78 | % | ASTM D638 |
彎曲模量 3 (1.97 in 跨距) | 338000 | psi | ASTM D790 |
彎曲強度 3 (屈服, 1.97 in 跨距) | 14100 | psi | ASTM D790 |
懸壁梁缺口沖擊強度 (73°F) | 7.0 | ft·lb/in | ASTM D256 |
無缺口懸臂梁沖擊 (73°F) | 60 | ft·lb/in | ASTM D4812 |
落錘沖擊 (73°F) | 1320 | in·lb | ASTM D3029 |
拉伸沖擊強度 4 | 275 | ft·lb/in2 | ASTM D1822 |
載荷下熱變形溫度 (264 psi, 未退火, 0.126 in) | 298 | °F | ASTM D648 |
線形熱膨脹系數(shù) - 流動 (-40 到 203°F) | 4.5E-5 | in/in/°F | ASTM E831 |
比熱 | 0.301 | Btu/lb/°F | ASTM C351 |
導熱系數(shù) | 1.5 | Btu·in/hr/ft2/°F | ASTM C177 |
RTI Elec | 266 | °F | UL 746 |
RTI Imp | 266 | °F | UL 746 |
RTI | 266 | °F | UL 746 |
體積電阻率 | > 2.5E+17 | ohms·cm | ASTM D257 |
介電強度 (0.126 in, in Air) | 510 | V/mil | ASTM D149 |
介電常數(shù) |
|
| ASTM D150 |
60 Hz | 3.27 |
|
|
50 kHz | 3.27 |
|
|
1 MHz | 3.10 |
|
|
耗散因數(shù) |
|
| ASTM D150 |
50 Hz | 1.6E-3 |
|
|
60 Hz | 1.6E-3 |
|
|
100 Hz | 0.026 |
|
|
耐電弧性 5 | PLC 6 |
| ASTM D495 |
相比耐漏電起痕指數(shù)(CTI) | PLC 3 |
| UL 746 |
高電弧燃燒指數(shù)(HAI) 6 | PLC 3 |
| UL 746 |
高電壓電弧起痕速率 (HVTR) | PLC 3 |
| UL 746 |
熱絲引燃 (HWI) | PLC 2 |
| UL 746 |
折射率 | 1.600 |
| ASTM D542 |
透射率 (100 mil) | 85.0 | % | ASTM D1003 |
霧度 (100 mil) | 1.0 | % | ASTM D1003 |
干燥溫度 | 248 | °F |
|
干燥時間 | 3.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
建議注射量 | 40 到 60 | % |
|
料筒后部溫度 | 617 到 662 | °F |
|
料筒中部溫度 | 644 到 680 | °F |
|
料筒前部溫度 | 662 到 698 | °F |
|
射嘴溫度 | 653 到 689 | °F |
|
加工（熔體）溫度 | 662 到 698 | °F |
|
模具溫度 | 176 到 239 | °F |
|
背壓 | 43.5 到 102 | psi |
|
螺桿轉速 | 40 到 70 | rpm |
|
排氣孔深度 | 9.8E-4 到 3.0E-3 | in |
|