CYCOLAC? Resin FR15U

Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate
Product No: CYCOLAC Resin FR15U
Product Quantity: 25KG / BAG
Product Features: Flame Retardant，Good Moldability，UV Resistant

Product information

CYCOLAC? Resin FR15U

Acrylonitrile Butadiene Styrene

SABIC Innovative Plastics

Product Description:

Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94V-0/5VA rated. Elevated UL RTI rating.

Features	Flame Retardant,Good Moldability,UV Resistant
Processing Method	Injection Molding
Multi-Point Data	Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)

Physical	Nominal Value	Unit	Test Method
Density / Specific Gravity
--	1.19		ASTM D792
--	1.19	g/cm3	ISO 1183
Melt Mass-Flow Rate (MFR)
230°C/3.8 kg	3.3	g/10 min	ASTM D1238
220°C/5.0 kg	7.0	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)	2.44	in3/10min	ISO 1133
Molding Shrinkage - Flow (0.126 in)	5.0E-3 to 7.0E-3	in/in	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- 3	300000	psi	ASTM D638
--	321000	psi	ISO 527-2/1
Tensile Strength
Yield 4	5500	psi	ASTM D638
Yield	5960	psi	ISO 527-2/50
Break 4	4400	psi	ASTM D638
Tensile Elongation
Yield 4	2.4	%	ASTM D638
Break 4	17	%	ASTM D638
Break	22	%	ISO 527-2/50
Flexural Modulus
1.97 in Span 5	340000	psi	ASTM D790
-- 6	328000	psi	ISO 178
Flexural Stress
-- 6, 7	9180	psi	ISO 178
Yield, 1.97 in Span 5	9800	psi	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
73°F	4.0	ft·lb/in	ASTM D256
73°F 8	5.7	ft·lb/in2	ISO 180/1A
Instrumented Dart Impact (73°F, Total Energy)	252	in·lb	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
66 psi, Unannealed, 0.126 in	187	°F
264 psi, Unannealed, 0.126 in	167	°F
Vicat Softening Temperature
--	201	°F	ASTM D1525 9
--	198	°F	ISO 306/B50
CLTE			ASTM E831
Flow : -40 to 104°F	5.0E-5	in/in/°F
Transverse : -40 to 104°F	5.1E-5	in/in/°F
RTI Elec	194	°F	UL 746
RTI Imp	185	°F	UL 746
RTI Str	194	°F	UL 746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	> 1.0E+14	ohms·cm	IEC 60093
Electric Strength (0.126 in, in Oil)	510	V/mil	IEC 60243-1
Arc Resistance 10	PLC 7		ASTM D495
Comparative Tracking Index (CTI)	PLC 1		UL 746
High Amp Arc Ignition (HAI)	PLC 4		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 4		UL 746
Hot-wire Ignition (HWI)	PLC 2		UL 746
Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.06 in	V-0
0.11 in	5VA

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (392°F, 1000 sec^-1)	320	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	180 to 190	°F
Drying Time	2.0 to 4.0	hr
Drying Time, Maximum	8.0	hr
Suggested Max Moisture	0.10	%
Suggested Shot Size	50 to 70	%
Rear Temperature	340 to 360	°F
Middle Temperature	390 to 410	°F
Front Temperature	400 to 430	°F
Nozzle Temperature	400 to 450	°F
Processing (Melt) Temp	400 to 450	°F
Mold Temperature	120 to 160	°F
Back Pressure	50.0 to 100	psi
Screw Speed	30 to 60	rpm
Vent Depth	1.5E-3 to 2.0E-3	in