Radiflam? A RV300 HF 339 NER
Polyamide 66
PA66 flame retardant injection moulding grade. Halogen and phosphorus free. Deep black colour.
Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance.
Good electrical insulating properties. Rated V-0 according to UL-94.
Filler / Reinforcement | |
Additive | |
Features | |
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.41 | -- | g/cm3 | ISO 1183 |
Tensile Modulus | 1.55E+6 | 1.28E+6 | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 22500 | 17400 | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 2.7 | 3.0 | % | ISO 527-2/1A/5 |
Flexural Modulus 3 | 1.42E+6 | -- | psi | ISO 178 |
Flexural Stress 3 | 34800 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 3.3 | -- | ft·lb/in2 |
|
73°F | 4.8 | 5.7 | ft·lb/in2 |
|
Charpy Unnotched Impact Strength |
|
|
| ISO 179/1eU |
-22°F | 33 | -- | ft·lb/in2 |
|
73°F | 31 | -- | ft·lb/in2 |
|
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 491 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 428 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 464 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 550 | -- | V | IEC 60112 |
Flame Rating (0.031 in) | V-0 | -- |
| UL 94 |
Glow Wire Flammability Index |
|
|
| IEC 60695-2-12 |
0.04 in | 1760 | -- | °F |
|
0.08 in | 1760 | -- | °F |
|
Glow Wire Ignition Temperature |
|
|
| IEC 60695-2-13 |
0.04 in | 1340 | -- | °F |
|
0.08 in | 1430 | -- | °F |
|
Flammability | 0 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.10 | % |
|
Processing (Melt) Temp | 527 to 554 | °F |
|
Mold Temperature | 176 to 194 | °F |
|
Injection Rate | Moderate-Fast |
|
|