Radiflam? A RV250 HF 100 NAT 1370
Polyamide 66
PA66 flame retardant injection moulding grade, halogen and red phosphorus free. 25% glass fiber reinforced. Natural colour.
Suitable for parts requiring fire retardancy along with medium stiffness and mechanical resistance. Good electrical insulating properties. Rated V-0 according to UL-94.
Filler / Reinforcement | |
Additive | |
Features | |
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.36 | -- | g/cm3 | ISO 1183 |
Molding Shrinkage 3 |
|
|
| ISO 294-4 |
Across Flow | 1.0 | -- | % |
|
Flow | 0.40 | -- | % |
|
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 5.5 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.3 | -- | % |
|
Tensile Modulus | 1.26E+6 | -- | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 19600 | -- | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 2.9 | -- | % | ISO 527-2/1A/5 |
Flexural Modulus 4 | 1.23E+6 | -- | psi | ISO 178 |
Flexural Stress 4 | 30500 | -- | psi | ISO 178 |
Charpy Unnotched Impact Strength(73°F) | 31 | -- | ft·lb/in2 | ISO 179/1eU |
Heat Deflection Temperature (264 psi, Unannealed) | 464 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 473 | -- | °F | ISO 306/B50 |
Melting Temperature 5 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 6 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 6 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Burning Rate (0.118 in) | 0.0 | -- | in/min | ISO 3795 |
Flame Rating (0.031 in) | V-0 | -- |
| UL 94 |
Glow Wire Flammability Index |
|
|
| IEC 60695-2-12 |
0.04 in | 1760 | -- | °F |
|
0.08 in | 1760 | -- | °F |
|
Glow Wire Ignition Temperature |
|
|
| IEC 60695-2-13 |
0.04 in | 1340 | -- | °F |
|
0.08 in | 1430 | -- | °F |
|
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | < -4 | °F |
|
Suggested Max Moisture | 0.10 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Mold Temperature | 176 to 212 | °F |
|
Injection Rate | Moderate-Fast |
|
|