Radilon? S RV300UK 339 E NER
Polyamide 6
PA6 30% glass fiber reinforced injection moulding grade. Improved UV resistance. Deep black colour.
Suitable for parts which must resist to outdoor exposure, requiring high stiffness, good mechanical resistance and good heat ageing properties retention.
ISO 1043 : PA6-T GF30
Filler / Reinforcement | |
Features | - Heat Aging Resistant，High Stiffness，UV Resistant，Weather Resistant
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.35 | -- | g/cm3 | ISO 1183 |
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.5 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 2.0 | -- | % |
|
Tensile Modulus | 1.39E+6 | 928000 | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 23900 | 15200 | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 3.1 | 4.0 | % | ISO 527-2/1A/5 |
Flexural Modulus 2 | 1.16E+6 | -- | psi | ISO 178 |
Flexural Stress 2 | 34800 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 3.8 | -- | ft·lb/in2 |
|
73°F | 4.8 | 7.1 | ft·lb/in2 |
|
Charpy Unnotched Impact Strength |
|
|
| ISO 179/1eU |
-22°F | 33 | -- | ft·lb/in2 |
|
73°F | 36 | 48 | ft·lb/in2 |
|
Heat Deflection Temperature (264 psi, Unannealed) | 392 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 410 | -- | °F | ISO 306/B50 |
Melting Temperature 3 | 428 | -- | °F | ISO 11357 |
Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index | 500 | -- | V | IEC 60112 |
Burning Rate | 0.0 | -- | in/min | FMVSS 302 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | < -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 464 to 536 | °F |
|
Mold Temperature | 176 to 194 | °F |
|
Injection Rate | Moderate-Fast |
|
|