Radilon? A RV150W 333 NER 6663
Polyamide 66
PA66 15% glass fiber reinforced injection moulding grade. Heat stabilized. Black colour.
Suitable for parts requiring improved stiffness and good heat ageing properties retention.
Filler / Reinforcement | |
Additive | |
Features | - Good Stiffness，Heat Aging Resistant，Heat Stabilized
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.23 | -- | g/cm3 | ISO 1183 |
Molding Shrinkage 2 |
|
|
| ISO 294-4 |
Across Flow | 0.90 | -- | % |
|
Flow | 0.40 | -- | % |
|
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.9 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 2.3 | -- | % |
|
Tensile Modulus | 841000 | 566000 | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 16700 | 12300 | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 2.5 | 4.0 | % | ISO 527-2/1A/5 |
Flexural Modulus 3 | 783000 | -- | psi | ISO 178 |
Flexural Stress 3 | 23900 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 2.6 | 2.9 | ft·lb/in2 |
|
73°F | 2.9 | 3.8 | ft·lb/in2 |
|
Charpy Unnotched Impact Strength(73°F) | 14 | 33 | ft·lb/in2 | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 464 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 419 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 473 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 500 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1200 | -- | °F | IEC 60695-2-12 |
Flammability | 0 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 536 to 572 | °F |
|
Mold Temperature | 176 to 212 | °F |
|
Injection Rate | Moderate |
|
|